1. 材料物性：

DuPont Elvax® 40W Ethylene-Vinyl Acetate Copolymer Resin

Material Notes:	Elvax® 40W has a higher vinyl acetate content compared with the other Elvax® resins resulting in higher elongation, reduced hardness, improved solubility and adhesion, and significant differences in compatibility. To minimize viscosity changes in hot melt blends during processing, Elvax® 40W also contains butylated hydroxytoluene(BHT). Elvax®40W is supplied in pellet form and to prevent the pellets from blocking, low levels of an amide wax have been added to the polymer. Typical Applications: Laminating adhesives for a variety of substrates including plastics and films. This grade provides the extended open time often needed in industrial assembly Lacquers for wood, metal, metal foils, paper, and films Fabric and decal coatings Heat-seal coatings for backing card stock used in blister packaging Wood primers and sealers. Combinations of Elvax® 40W and nitrocellulose form the basis for wood sealers offering toughness and good intercoat adhesion Elvax® 40W is also suggested for use as a modifier in: Elastomer-based hot melt and hot melt pressure-sensitive adhesion formulations Natural and synthetic elastomers to improve resistance to ozone cracking Caulks and sealants, including those based on asphalt Asphalt road repairing compositions for resurfacing, patching, and crack sealing to improve low temperature flexibility, strength properties, and adhesion Traffic paint formulations Solvent-based and wax-based inks

Material Notes:

Elvax® 40W has a higher vinyl acetate content compared with the other Elvax® resins resulting in higher elongation, reduced hardness, improved solubility and adhesion, and significant differences in compatibility. To minimize viscosity changes in hot melt blends during processing, Elvax® 40W also contains butylated hydroxytoluene(BHT). Elvax®40W is supplied in pellet form and to prevent the pellets from blocking, low levels of an amide wax have been added to the polymer.

Typical Applications:

Laminating adhesives for a variety of substrates including plastics and films. This grade provides the extended open time often needed in industrial assembly
Lacquers for wood, metal, metal foils, paper, and films
Fabric and decal coatings
Heat-seal coatings for backing card stock used in blister packaging
Wood primers and sealers. Combinations of Elvax® 40W and nitrocellulose form the basis for wood sealers offering toughness and good intercoat adhesion

Elvax® 40W is also suggested for use as a modifier in:

Elastomer-based hot melt and hot melt pressure-sensitive adhesion formulations
Natural and synthetic elastomers to improve resistance to ozone cracking
Caulks and sealants, including those based on asphalt
Asphalt road repairing compositions for resurfacing, patching, and crack sealing to improve low temperature flexibility, strength properties, and adhesion
Traffic paint formulations
Solvent-based and wax-based inks

特性备注：VAC含量40%

重要参数：熔体流动速率:65 g/10min 密度:0.97 g/cm3

Material Notes: Elvax® 40W has a higher vinyl acetate content compared with the other Elvax® resins resulting in higher elongation, reduced hardness, improved solubility and adhesion, and significant differences in compatibility. To minimize viscosity changes in hot melt blends during processing, Elvax® 40W also contains butylated hydroxytoluene(BHT). Elvax®40W is supplied in pellet form and to prevent the pellets from blocking, low levels of an amide wax have been added to the polymer.

Typical Applications:

•Laminating adhesives for a variety of substrates including plastics and films. This grade provides the extended open time often needed in industrial assembly
•Lacquers for wood, metal, metal foils, paper, and films
•Fabric and decal coatings
•Heat-seal coatings for backing card stock used in blister packaging
•Wood primers and sealers. Combinations of Elvax® 40W and nitrocellulose form the basis for wood sealers offering toughness and good intercoat adhesion
Elvax® 40W is also suggested for use as a modifier in:
•Elastomer-based hot melt and hot melt pressure-sensitive adhesion formulations
•Natural and synthetic elastomers to improve resistance to ozone cracking
•Caulks and sealants, including those based on asphalt
•Asphalt road repairing compositions for resurfacing, patching, and crack sealing to improve low temperature flexibility, strength properties, and adhesion
•Traffic paint formulations
•Solvent-based and wax-based inks

Pict Physical Properties	Metric	English	Comments
Density	0.965 g/cc	0.0349 lb/in³	ASTM D1505
Viscosity Measurement	0.7	0.7	Inherent, 0.25 g/100mL toluene
Viscosity Measurement	@Temperature 30.0 °C	@Temperature 86.0 °F	Inherent, 0.25 g/100mL toluene
Vinyl Acetate Content	40%	40%	DuPont Method
Melt Index of Compound	52 g/10 min	52 g/10 min	ASTM D1238, modified

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	40	40	10 seconds, Shore A-2; ASTM D2240
Tensile Strength at Break	4.80 - 6.20 MPa	696 - 899 psi	Samples die cut from pressed films, gage dimensions 2.23cm x 0.47cm x 0.13cm, crosshead speed 2in/min; ASTM D1708
Elongation at Break	1000 - 1300 %	1000 - 1300 %	Samples die cut from pressed films, gage dimensions 2.23cm x 0.47cm x 0.13cm, crosshead speed 2in/min; ASTM D1708
Tensile Modulus	0.00300 GPa	0.435 ksi	Samples die cut from pressed films, gage dimensions 2.23cm x 0.47cm x 0.13cm, crosshead speed 2in/min; ASTM D638

Thermal Properties	Metric	English	Comments
Ring & Ball Softening Point	104 °C	219 °F	ASTM E28

Descriptive Properties
Antioxidant	550 ppm	BHT
Odor	Slight
Residual VA Monomer, wt%	<0.3
Vinyl Acetate Content	40 wt.%	DuPont Method

品名：涂覆用EVA
单价： [查看报价如果没找到请来电询价]
最小起订： 25KG
供货总量： 100000000
发货期限：自买家付款之日起 1 天内发货
联系人：王先生
公司电话： 0769-87190386/13662834186
即时通讯： qq:249911599. 微信：ydsujiao
公司保障：公司已经在百度做了实名认证和阿里巴巴的诚信通以及国家工信部实名备案
买家保障：亿鼎公司已经开通买家保障服务，当前保证金金额为：5000元。
可15天包换，支持7天退货。

2. 类似的材料列表：

加拿大AT	2820A	28% VAC	涂覆用
加拿大AT	2830A	28% VAC	涂覆用
加拿大AT	2842A	28% VAC	涂覆用
加拿大AT	4030AC	40% VAC	涂覆用
巴西Braskem	HM2528	28% VAC	涂覆用

：0.00元/

立即购买

最新产品

产品分类

涂覆用EVA

涂覆用EVA

相关产品